Base requirements and coating conditions
The strength class of the concrete must be at least C25/30 and the wear resistance class 3. The relative humidity of the concrete must be below 95% and the surface temperature must be at least +3⁰C above dewpoint. During the drying of the coating, the temperature of the ambient air, the surface and the coating must be over +15⁰C and relative humidity must be below 80%.
New concrete floor
Laitance and any uncured cement are removed by either surface grinding or shot blasting. All loose material that could negatively affect adhesion is removed, and cement dust is carefully vacuum-cleaned.
Old concrete floor
Laitance and damaged concrete are removed by grinding or shot blasting. All loose material that could negatively affect adhesion is removed, and the base is carefully vacuum-cleaned. Dirty floors should be washed and rinsed with synthetic detergent before performing any other base treatment work. Any old coat is removed completely.
Priming
Priming is carried out using Nanten HM Epoxy. On damp concrete substrates with a relative humidity above 95%, a moisture-tolerant primer such as Nanten M Primer must be used. The primer must seal all pores in the concrete and form a uniform, dense, and continuous film. Small holes and cracks must be cleaned and filled with epoxy putty made from Nanten HM Epoxy and fine filler sand. If necessary, uneven surfaces must be levelled using an epoxy screed. ESD coating systems require an even substrate.
ESD Priming treatment
Copper grounding tapes must be applied according to the installation plan on the cured surface of HM Epoxy. Each room must have two grounding points. The actual primer in Nanten ESD coating systems is the conductive Nanten ESD Primer.
ESD Priming
The mixed material is poured onto the floor in a continuous ribbon and spread with a roller. Conductive ESD quartz sand is broadcast onto the wet primer to improve adhesion of the coating and facilitate the application of the ESD trowel coating. The consumption of ESD Primer must be more than 0.35 l/m². The primer coat must be uniform in thickness.
Mixing
Pre-mix Part A and Part B of the ESD Primer separately in their original containers. Then combine the components in a mixing vessel and mix with a low-speed mixer for approximately two minutes, avoiding air entrapment in the mixture.
Spreading rate
Part A: 5 parts by volume
Part B: 1 part by volume
Always mix both components together thoroughly.
Coverage
Consumption approx. 0.35 l/m².